Aluminum Panel Bonding 2K-PU Adhesive

Product Details
Customization: Available
Bonding Function: Structural Adhesive
Morphology: Solid-State
Still deciding? Get samples of US$ 0.01/Set
Request Sample
Diamond Member Since 2011

Suppliers with verified business licenses

Audited Supplier

Audited by an independent third-party inspection agency

Importers and Exporters
The supplier has import and export rights
Years of Export Experience
The export experience of the supplier is more than 10 years
Multi-language Pioneer
3 languages freely used by foreign trade staff. include: English, Arabic, Russian
Exhibition Experience
The supplier had participated in offline trade shows, you can check the Audit Report for more information
to see all verified strength labels (33)
  • Aluminum Panel Bonding 2K-PU Adhesive
  • Aluminum Panel Bonding 2K-PU Adhesive
  • Aluminum Panel Bonding 2K-PU Adhesive
Find Similar Products

Basic Info.

Model NO.
Flexibond8207
Material
Polyurethane
Classification
Room Curing
Main Agent Composition
Polyurethane Elastomer
Characteristic
Waterproof
Promoter Composition
Curing Agent
Composition
Organic Material
Color
Yellow
Transport Package
25kg/5kg Cubo 1250kg/250kg Tambor
Specification
25kg/5kg Cubo 1250kg/250kg Tambor
Trademark
Flexibond
Origin
China
HS Code
3909500000
Production Capacity
50000 Tons/Year

Product Description

Flexibond 8207

Technical data
  Component A(Resin) Component B(Hardener)
Curing mechanism Poly addition
Chemical base Multiplehydroxyl compound PAPI
Color White Brown
The color after mixing Light yellow
Density (before curing) 1.6g/ cm3 1.2g/ cm3
Viscosity 10000-15000mpa.s
(Brookfield - RVT 6/20)
200-300mpa.s (Brookfield - RVT 2/50)
Viscosity (after mixing) 4000-6000mpa.s (Brookfield - RVT 6/20)
Mixing ratio (by weight) 100 20
Pot life (23°C) 40-60 mins
Open time (23°C, 50%RH) 65-80 mins
Hardness shore D (GB/T 531-2008) Approx 65
Shear strength (GB/T 7124-2008) ≥ 10Mpa (Aluminum alloy)
Shelf life (unopened below 25°C) 12 months 6 months
*Testing temperature 23°C and 50% r.h.

1.Description:
Flexibond 8207 is a two-component polyurethane adhesive which is suitable for sandwich structural bonding, and for various substrates, such as wood, glass fiber panel, aluminum panel, steel panel bonding to various honeycomb structure, polyurethane sandwich panel, polystyrene foam board, etc. The adhesive is solvent free, environmental friendly.

2.Characteristics:
(1)Excellent adhesion to various substrates without bubble.
(2)Cures fast, shortens heated or cold setting time.
(3)Suitable for scraping operation.
(4)No irritant gas forming.
(5)Good humidity and heat resistance.

3.Application

(1)Preparation:
Prepare an empty drum. Request: clean and dry. Mixing tool: Sticks for manual mixing or electric mixer.
Electronic scale: It would be better if the electronic scale can accurately weighting to a decimal point.

(2)Surface Treatment of the Substrates:
The substrates should be clean and dry and of no grease, dust, or other contaminations. The substrates can be cleaned by ethanol, a-cetone. If the metal surface is coated with primer, the discharged agent on the plastic surface is cleaned, or the surface is polished, the adhesion can be increased significantly.

(3)Flexibond 8207/Flexibond 8200=5:1 (by weight)
The resin (component A) should be uniformly mixed before its mixing with the hardener (component B). Mix for 1-2 more minutes after the two component color is well mixed. Use up the mixer as soon as possible before its pot life, or less frequent principle can be taken.

(4)Adhesive Coating:
The adhesive can be coated with serrated scrapers manually or rollers. The adhesive should be coated uniformly on the substrate surface. The recommended dosage is 200-400g/m2. The dosage varies with the roughness of the substrate surface.
The adhesive should be coated within its pot life. The specifications can be referred to Figure 1.

(5)Pressing:
Substrates have been coated with adhesive should be pressed within open time, or the adhesion strength will be affected. Raise the compounding pressure as high as possible without affecting the material forming. The specifications can be referred to Figure 1.Aluminum Panel Bonding 2K-PU Adhesive
                             Figure 1                                                         Figure 2
(6)Pressing time
The curing speed and the time to form adhesion vary with the temperature. The curing speed is slower and it takes longer time for pressing as the temperature is lower; the curing speed is faster and it takes shorter time for pressing as the temperature is higher. The pressing time is 5 hours under 23°C. The specifications can be referred to Figure 2.
(7)Working Condition
Recommended working condition: temperature 5-30°C, relative humidity <80°C. The curing speed will be affected if the temperature is too low. And too much bubble will be formed if the humidity it too high.
(8)Clean
Recommended Cleaner: a-cetone, butanone.

4.Packaging
Resin: 25kg/drum Hardener: 25kg/drum
Resin: 1250kg/pail Hardener: 250kg/pail
The packaging can be adjusted according to customer's requirement.



5.Shear Strength Chart:
Aluminum Panel Bonding 2K-PU Adhesive


Heating performance of the adhesive:
Tensile Shear strength (in MPa) as function of the curing time at elevated temperatures
Curing temperature 20mins 30mins 1hours 3 hours 5 hours 7 hours
80°C 6.3 7.4 8.5 9.5 10.1 10.8
100°C 8.1 8.9 9.6 10.3 10.8 11.5
120°C 9.4 9.8 10.6 11.3 11.6 12.2


6.Note
(1)The adhesive sealant should be used up once mixed. The remaining sealant cannot be used if viscosity appears too large or its state is like jelly.
(2)Do not apply the product together with other adhesives. Please enquire to our technicians if you have such a need.
(3)The information and recommendations related to the application and end-use of COMENS' products are given in good faith based on COMENS' current knowledge and experience of the products when properly stored, handled and applied under normal conditions. This information must on no account be used as a substitute for necessary prior tests which alone can ensure that a product is suitable for a given use, due to the practical differences in materials, substrates and actual site conditions. Users are requested to check that they are in possession of the latest version of this documents and COMENS' is at their disposal to supply any additional information.


Beijing Comens New Materials Co. Ltd
Add: No. 8, Yanshan Industrial Zone, Fangshan District, Beijing, China







 

Send your message to this supplier

*From:
*To:
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now
Contact Supplier